炭化MFCの炭素前躯体樹脂への添加によるC/C複合材料の機械的特性の向上
https://doi.org/10.14988/pa.2017.0000012261
https://doi.org/10.14988/pa.2017.0000012261206bdaef-2e0a-44c5-bf8b-2ab31b12842e
| 名前 / ファイル | ライセンス | アクション |
|---|---|---|
023051030004.pdf (564.3 kB)
|
|
| Item type | 紀要論文 / Departmental Bulletin Paper(1) | |||||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| 公開日 | 2010-11-25 | |||||||||||||||||
| タイトル | ||||||||||||||||||
| タイトル | 炭化MFCの炭素前躯体樹脂への添加によるC/C複合材料の機械的特性の向上 | |||||||||||||||||
| 言語 | ja | |||||||||||||||||
| タイトル | ||||||||||||||||||
| タイトル | タンカ MFC ノ タンソ ゼンクタイ ジュシ エノ テンカ ニヨル C/C フクゴウ ザイリョウ ノ キカイテキ トクセイ ノ コウジョウ | |||||||||||||||||
| 言語 | ja-Kana | |||||||||||||||||
| タイトル | ||||||||||||||||||
| タイトル | Improvement of mechanical properties of C/C composite by addition of carbonized MFC into carbon precursor | |||||||||||||||||
| 言語 | en | |||||||||||||||||
| 言語 | ||||||||||||||||||
| 言語 | jpn | |||||||||||||||||
| キーワード | ||||||||||||||||||
| 主題 | 炭素繊維強化炭素複合材料, 炭素繊維, ミクロフィブリル化セルロース, 凍結乾燥, 曲げ強度, 破壊じん性 C/C composites, Carbon Fiber, MFC, Freeze-drying, Bending Strength, Fracture Toughness |
|||||||||||||||||
| 資源タイプ | ||||||||||||||||||
| 資源タイプ識別子 | http://purl.org/coar/resource_type/c_6501 | |||||||||||||||||
| 資源タイプ | departmental bulletin paper | |||||||||||||||||
| ID登録 | ||||||||||||||||||
| ID登録 | 10.14988/pa.2017.0000012261 | |||||||||||||||||
| ID登録タイプ | JaLC | |||||||||||||||||
| アクセス権 | ||||||||||||||||||
| アクセス権 | open access | |||||||||||||||||
| アクセス権URI | http://purl.org/coar/access_right/c_abf2 | |||||||||||||||||
| 著者 |
小武内, 清貴
× 小武内, 清貴
WEKO
2306
× 竹内, 康徳× 大窪, 和也× 藤井, 透
WEKO
16551
|
|||||||||||||||||
| 著者所属 | ||||||||||||||||||
| 言語 | ja | |||||||||||||||||
| 値 | 小武内, 清貴 / PhD student, JSPS Research Fellow, Department of Mechanical Engineering and Systems, Doshisha University | |||||||||||||||||
| 著者所属 | ||||||||||||||||||
| 言語 | ja | |||||||||||||||||
| 値 | 竹内, 康徳 / Graduate student, Department of Biomedical Engineering, Doshisha University | |||||||||||||||||
| 著者所属 | ||||||||||||||||||
| 言語 | ja | |||||||||||||||||
| 値 | 大窪, 和也 / 同志社大学理工学部教授 | |||||||||||||||||
| 著者所属 | ||||||||||||||||||
| 言語 | ja | |||||||||||||||||
| 値 | 藤井, 透 / 同志社大学理工学部教授 | |||||||||||||||||
| 著者所属（英） | ||||||||||||||||||
| 言語 | en | |||||||||||||||||
| 値 | Doshisha University | |||||||||||||||||
| 所属機関識別子種別 | ||||||||||||||||||
| 値 | kakenhi | |||||||||||||||||
| 所属機関識別子 | ||||||||||||||||||
| 値 | 34310 | |||||||||||||||||
| 抄録 | ||||||||||||||||||
| 内容記述タイプ | Abstract | |||||||||||||||||
| 内容記述 | 本研究の目的はC/C複合材料の機械的特性を炭化MFCを添加することによって向上する手法を提案することである.本研究ではフェノール樹脂を母材とするCFRPを不活性雰囲気中,1,000℃で熱処理を行うことによってC/C複合材料を得た.炭化MFCの添加率の違いによる曲げ強度の違いを考察した.MFCを添加したC/C複合材料の機械的特性を万能材料試験機,水銀ポロシメータ等を用いて評価した.試験結果より,炭化MFCの1wt%の添加によって,曲げ強度が大きく向上することがわかった.また過度の炭化MFCの添加は曲げ強度の向上に有効でないこともわかった.破壊面を観察した結果,1wt%の添加条件において,繊維破断が観察された.それ以外の条件では剥離が観察された.SEM観察によって1wt%の添加条件において,炭化MFCの力学的なブリッジングがENFテストによって評価したモードII破壊じん性の向上に有効であることがわかった. | |||||||||||||||||
| 言語 | ja | |||||||||||||||||
| 抄録 | ||||||||||||||||||
| 内容記述タイプ | Abstract | |||||||||||||||||
| 内容記述 | The purpose of this study is to propose an effective technique to improve the mechanical properties of C/C composites by adding carbonized MFC into carbon precursor. In this study, conventional CFRP was carbonized at 1,000˚C with inert atmosphere to fabricate the C/C composites in which pyrocarbon matrix was made from phenolic resin. Effect of weight content of carbonized MFC on the bending strength was discussed. The modified C/C composites were mechanically characterized by using a universal testing machine and mercury porosimeter. Test results showed that the significant improvement in the bending strength was appeared at condition of 1.0 wt% of addition, while the excessive addition of carbonized MFC was not effective to improve the bending strength. The morphology evaluation of fracture surface was revealed that the fiber braking was observed at the condition of 1.0 wt% of addition, while delamination was appeared on that of unmodified, 3.0 and 5.0 wt% of carbonized MFC addition. The SEM observation also revealed that local bridging of carbonized MFC was effective to improve the modeII fracture toughness evaluated by ENF (End Notch Failure) test when the 1wt% of carbonized MFC was added. | |||||||||||||||||
| 言語 | en | |||||||||||||||||
| 書誌情報 |
ja : 同志社大学理工学研究報告 en : The Science and Engineering Review of Doshisha University 巻 51, 号 3, p. 26-31, 発行日 2010-10-31 |
|||||||||||||||||
| 出版者 | ||||||||||||||||||
| 出版者 | 同志社大学理工学研究所 | |||||||||||||||||
| 言語 | ja | |||||||||||||||||
| 出版者（英） | ||||||||||||||||||
| 出版者 | Science and Engineering Research Institute of Doshisha University | |||||||||||||||||
| 言語 | en | |||||||||||||||||
| ISSN | ||||||||||||||||||
| 収録物識別子タイプ | PISSN | |||||||||||||||||
| 収録物識別子 | 00368172 | |||||||||||||||||
| 書誌レコードID | ||||||||||||||||||
| 収録物識別子タイプ | NCID | |||||||||||||||||
| 収録物識別子 | AN00165868 | |||||||||||||||||
| 権利者情報 | ||||||||||||||||||
| 権利者識別子Scheme | AID | |||||||||||||||||
| 権利者識別子 | DA03974933 | |||||||||||||||||
| 権利者名 | 同志社大学理工学研究所 | |||||||||||||||||
| 言語 | ja | |||||||||||||||||
| 権利者名 | Science and Engineering Research Institute of Doshisha University | |||||||||||||||||
| 言語 | en | |||||||||||||||||
| 関連サイト | ||||||||||||||||||
| 関連タイプ | isFormatOf | |||||||||||||||||
| 識別子タイプ | URI | |||||||||||||||||
| 関連識別子 | https://doors.doshisha.ac.jp/opac/opac_link/bibid/SB00960326/?lang=0 | |||||||||||||||||
| 言語 | ja | |||||||||||||||||
| 関連名称 | 掲載刊行物所蔵情報へのリンク ／ Link to Contents | |||||||||||||||||
| フォーマット | ||||||||||||||||||
| 内容記述タイプ | Other | |||||||||||||||||
| 内容記述 | application/pdf | |||||||||||||||||
| 出版タイプ | ||||||||||||||||||
| 出版タイプ | VoR | |||||||||||||||||
| 出版タイプResource | http://purl.org/coar/version/c_970fb48d4fbd8a85 | |||||||||||||||||
| 日本十進分類法 | ||||||||||||||||||
| 主題Scheme | NDC | |||||||||||||||||
| 主題 | 501.49 | |||||||||||||||||